TABLA 7-. REQUISITOS DE CALIDAD PARA EMULSIONES ASFALTICAS
CATIONICAS |
|
|
|
|
|
|
|
|
|
|
|
|
|
CARACTERISTICAS |
CLASIFICACION |
|
DE LA EMULSION: |
|
ECR-60 |
ECR-65 |
ECR-70 |
ECM-65 |
ECL-65 |
ECI-45 |
ECS-60 |
|
CONTENIDO DE CEMENTO |
60 |
65 |
68 |
65 |
65 |
60 |
60 |
|
ASFALTICO EN MASA; % MINIMO |
|
VISCOSIDAD SAYBOLT-FUROL A |
--- |
--- |
--- |
--- |
25 |
5 |
25 |
|
25°C; S, MINIMO |
|
|
VISCOSIDAD SAYBOLT-FUROL A |
5 |
40 |
50 |
25 |
--- |
--- |
--- |
|
50°C, S, MINIMO. |
|
|
ASENTAMIENTO EN 5 DIAS; |
5 |
5 |
5 |
5 |
5 |
10 |
5 |
|
DIFERENCIA EN %, MINIMO |
|
RETENIDO EN MALLA N° 20 EN LA |
0,1 |
0,1 |
0,1 |
0,1 |
0,1 |
0,1 |
0,1 |
|
PRUEBA DEL TAMIZ; % MAXIMO |
|
PASA MALLA N° 20 Y SE RETIENE |
0,25 |
0,25 |
0,25 |
0,25 |
0,25 |
0,25 |
0,25 |
|
EN MALLA N°60 EN LA PRUEBA |
|
DEL TAMIZ; % MAXIMO |
|
|
CUBRIMIENTO DEL AGRGADO |
--- |
--- |
--- |
90 |
90 |
--- |
90 |
|
SECO; MINIMO |
|
|
CUBRIMIENTO DEL AGRGADO |
--- |
--- |
--- |
75 |
75 |
--- |
75 |
|
SECO; %, MINIMO |
|
|
CARGAS ELECTRICAS DE LAS |
(+) |
(+) |
(+) |
(+) |
(+) |
(+) |
(+) |
|
PARTICULAS |
|
|
DISOLVENTE EN VOLUMEN; %, |
--- |
3 |
5 |
5 |
--- |
15 |
--- |
|
MAXIMO |
|
|
|
INDICE DE RUPTURA; % |
|
< 100 |
<100 |
80-40 |
80-140 |
>120 |
--- |
>120 |
|
DEL RESIDUO DE LA DESTILACION |
|
|
|
|
|
|
|
|
VISCOSIDAD DINAMICA A 60°C; |
50+/-10(500+/-100) |
50+/-10(500+/-100) |
50+/-10(500+/-100) |
50+/-10(500+/-100) |
50+/-10(500+/-100) |
50+/-10(500+/-100) |
50+/-10(500+/-100) |
|
PA . S
(P [1] |
) |
|
|
PENETRACION [2]
A 25° C, EN |
110-250 |
110-250 |
110-250 |
100-250 |
100-250 |
100-400 |
100-250 |
|
100 G Y 5 S; 10-1
MM |
|
|
SOLUBILIDAD; %, MINIMO |
97,5 |
97,5 |
97,5 |
97,5 |
97,5 |
97,5 |
--- |
|
DUCTIBILIDAD A 25 °C; MINIMO |
40 |
40 |
40 |
40 |
40 |
40 |
--- |
|
|
|
|
|
|
|
|
|
|
|
|
[1] POISES |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TABLA 8.- REQUISITOS DE CALIDAD PARA ASFALTOS REBAJADOS |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
CARACTERISTICAS |
GRADO |
|
DEL ASFALTO REBAJADO |
|
|
|
PUNTO DE INFLAMACION TAG; °C, MINIMO |
38 |
27 |
|
VISCOSIDAD SAYBOLT-FUROL A 50 °C;S |
75-150 |
--- |
|
VISCOSIDAD SAYBOLT-FUROL A 60 °C;S |
--- |
250-500 |
|
CONTENIDO DE SOLVENTE POR DESTILACVION A 360°CC, EN VOLUMEN;% |
|
|
|
HASTA 225 °C |
20 MAX |
25 MIN |
|
HASTA 260 °C |
25-65 |
55 MIN |
|
HASTA 315 °C |
70-90 |
83MIN |
|
CONTENIDO DE CEMENTO ASFALTICO POR DESTILACION A 360°C, EN VOLUMEN,
%, MINIMO |
60 |
73 |
|
CONTENIDO DE AGUA POR DESTILACION A 360°C, EN VOLUMEN, %, MAXIMO |
0,2 |
0,2 |
|
DEL RESIDUO DE LA DESTILACION |
|
|
|
VISCOSIDAD DINAMICA A 60°C; PA .
S (P [1]
), MAXIMO |
200+/-40(200+/-400) |
200+/-40(2 000+/-400) |
|
PENETRACION A 25°C, EN 100 G Y 5 S; 10 -1
MM |
120-300 |
80-12 |
|
DUCTIBILIDAD A 25°C; CM; MINIMO |
100 |
100 |
|
SOLUBILIDAD; %MINIMO |
99,5 |
99,5 |
|
|
TABLA 3.- REQUISITOS DE CALIDAD PARA EMULSION ASFALTICA MODIFICADA |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
CARACTERISTICAS |
VALOR |
|
DE LA EMULSION: |
|
|
CONTENIDO DE CEMENTO ASFALTICO EN MASA; %, MINIMO |
60 |
|
VISCOSIDAD SAYBOLT- FUROL A 50 °C; S |
50-200 |
|
ASENTAMIENTO EN 5 DIAS; DIFERENCIA EN %, MAXIMO |
3 |
|
RETENIDO DE PESO EN MALLA N° 20 EN LA PRUEBA DE TAMIZ; %, MAXIMO |
0,1 |
|
CARGA ELECTRICA DE LAS PARTICULAS |
(+) |
|
DISOLVENTE EN VOLUMEN; %, MAXIMO |
3 |
|
DEMULSIBILIDAD; % MINIMO |
60 |
|
INDICE DE RUPTURA; % |
80-140 |
|
DEL RESIDUO DE LA DESTILACION: |
|
|
PENETRACION A 25° C, EN 100 G Y 5 S ; 10 -1
MM |
100-200 |
|
DUCTIBILIDAD A 4°C, 5 CM/MIN; CM, MINIMO |
30 |
|
RECUPERACION ELASTICA EN DUCTILOMETRO A 25°C, 20 CM, 5 MIN; %,
MINIMO |
40 |
|
RECUPERACION ELASTICA EN DUCTILOMETRO A 25°C, 10 CM, 5 MIN; %,
MINIMO |
50 |
|
|
|
|
|
|
TABLA 1-. REQUISITOS DE CALIDAD PARA CEMENTOS ASFALTICOS AC-5 Y
AC-20 MODIFICADOS |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TIPO DE CEMENTO ASFALTICO (TIPO DE MODIFICADOR) |
|
CARACTERISTICAS |
AC-5 (TIPO I Ó II |
AC-20(TIPO I) |
AC-20 (TIPO II) |
AC-20 (TIPO III ) |
AC-20 (HULE MOLIDO) |
|
DEL CEMENTO ASFALTICO MODIFICADO: |
|
|
VISCOSIDAD SAYBOLT-FUROL A 135 °C;S, MAXIMO |
500 |
1000 |
1000 |
1000 |
--- |
|
VISCOSIDAD ROTACIONAL BROOKFIELD A 135°C ; PA S, MAXIMO |
2 |
4 |
3 |
4 |
--- |
|
VISCOSIDAD ROTACIONAL BROOKFIELD (TIPO HAAKE) A 177°C; PA S, MAXIMO |
--- |
--- |
--- |
--- |
7 |
|
PENETRACION |
|
|
A25°C, 100 G, 5 S; 10 -1MM,
MINIMO |
80 |
40 |
40 |
30 |
30 |
|
A 4°C, 200 G, 60 S; 10-1
MM,MINIMO |
40 |
25 |
25 |
20 |
15 |
|
PUNTO DE INFLAMACION CLEVELAND;°C, MINIMO |
220 |
230 |
230 |
230 |
230 |
|
PUNTO DE REBLANDECIMIENTO; °C, MINIMO |
45 |
55 |
55 |
53 |
57 |
|
SEPARACION, DIFERENCIA ANILLO Y ESFERA; °C, MAXIMO |
3 |
3 |
3 |
4 |
5 |
|
RECUPERACION ELASTICA POR TORSION A 25°C; %, MINIMO |
25 |
30 |
30 |
15 |
40 |
|
RESILENCIA, A 25°C;%, MINIMO |
20 |
20 |
20 |
25 |
30 |
|
DEL RESIDUO DE LA PRUEBA DE LA PELICULA DELGADA, (3,2 MM, G): |
|
|
PERDIDA POR CALENTAMIENTO A 163°C;%, MAXIMO |
1 |
1 |
1 |
1 |
1 |
|
DUCTIBILIDAD A 4°C Y 5 CM/MIN;CM, MINIMO |
10 |
7 |
10 |
5 |
5 |
|
PENETRACION A 4°C, 200 G, 60 S; 10 -1
MM, MINIMO |
--- |
--- |
--- |
--- |
10 |
|
PENETRACION RETENIDA A 4°C, 200 G, 60 S; %, MINIMO |
65 |
65 |
65 |
55 |
75 |
|
RECUPERACION ELASTICA EN DUCTILOMETRO A 25°C;%, MINIMO |
50 |
50 |
60 |
30 |
55 |
|
INCREMENTO EN TEMPERATURA ANILLO Y ESFERA;°C, MAXIMO |
--- |
--- |
--- |
--- |
10 |
|
MODULO REOLOGICO DE CORTE DINAMICO A 76°C (G*/SEN s); K PA, MINIMO |
--- |
2,2 |
2,2 |
2,2 |
2,2 |
|
MODULO REOLOGICO DE CORTE DINAMICO A 64°C (G*/SEN s); KPA MINIMO |
2,2 |
--- |
--- |
--- |
--- |
|
ANGULO FASE (s) [visco-elasticidad], A 76°C; ° (GRADOS), MAXIMO |
--- |
75 |
70 |
75 |
--- |
|
ANGULO FASE (s) [VISCO-ELASTICIDAD], A 64°C:° (GRADOS), MAXIMO |
75 |
--- |
--- |
--- |
--- |
|
|